Mikovaa and Robert Z. Penb , * aInstitute of Chemistry and Chemical Technology SB RAS 50-24 Akademgorodok, Krasnoyarsk, 660036, Russia b Received 24.03.2015, received in revised form 15.04.2015, accepted 15.05.2015 The method of experimental statistical analysis was applied to study the effect of mass ratio of phenol and lignin (factor X1 X2 ) and the weight ratio of thereof mixture with formaldehyde (factor ) on the values of specifi c parameters of the porous structure obtained organic lignin – phenolformaldehyde aerogels. <...> Under optimal values of X1 macropore volume of 4.05 cm3 specifi c surface area and mesopore volume of obtained organic aerogels are 485 m2 cm3 = 0.25, and X2 /g and total pore volume – 4.67 cm 3 = 1,7 the maximum predicted values of the /g and 1,83 = 1.25 calculated values reach a /g. <...> Keywords: lignin, formaldehyde, lignin – phenol- formaldehyde gel, optimization process, mathematical model, porous structure, surface area, pore volume. <...> All rights reserved * Corresponding author E-mail address: inm@icct.ru Siberian State Technological University 82 Mira, Krasnoyarsk, 660049, Russia # 287 # Nadezhda M. <...> Optimization of the Process of Synthesis of Lignin – Phenol. <...> Мира, 82 Методом экспериментально-статистического анализа изучено влияние массового соотношения фенола и лигнина (Х1 (Х2 ) и массового соотношения их смеси с формальдегидом ) на значения параметров пористой структуры получаемых органических лигнинфенол-формальдегидный аэрогелей. <...> На основании оценки полученной математической модели установлено, что при соблюдении условий Х1 = 0,65-0,78, а Х2 /г и 1,85 г/см3 Х1 = 0,25, а Х2 = 1,25 рассчитанные значения объема макропор достигают 4,05 см3 объема пор – 4,67 см3 /г. Ключевые слова: лигнин, формальдегид, лигнин-фенол-формальдегидный гель, процесс оптимизации, математическая модель <...>